5086 is a marine-grade aluminum-magnesium alloy (AlMg4) valued for its seawater corrosion resistance and weldability. It is a non-heat-treatable 5xxx grade supplied in sheet, plate, bar, tube, and wire across O, H111, H112, H116, H321, and H32 tempers for shipbuilding, tanks, and welded structures.
Formularios disponibles: chapa / placa / barra / tubo / alambre / bobina
Temperamentos habituales: O, H111, H112, H116, H321, H32
Asistencia técnica: mecanizado CNC / corte por láser / soldadura / anodizado
Documentos de calidad: Informe MTC con cada pedido
5086 Aluminum Alloy (AlMg4) is a non-heat-treatable aluminum-magnesium (5xxx) alloy. Its strength comes from magnesium in solid solution and strain hardening, not heat treatment. It offers good corrosion resistance—especially in marine and industrial environments—and welds well, which makes it a common choice for structures exposed to water, chemicals, or cycling loads.
5086 Aluminum Alloy is supplied in several forms and tempers. Standard size ranges are below; other dimensions can be discussed with our team.
| Elemento | Rango |
|---|---|
| Espesor | 0,5 – 150 mm |
| Anchura | 1000 – 3000 mm |
| Longitud | 1000 – 6000 mm |
| Temple comunes | O, H111, H112, H116, H321, H32 |
| Elemento | Rango |
|---|---|
| Diámetro / lado | 6 – 400 mm |
| Longitud | 1000 – 6000 mm |
| Temple comunes | O, H111, H112, H116, H321, H32 |
| Elemento | Rango |
|---|---|
| Diámetro exterior | 6 – 400 mm |
| Espesor de pared | 0,5 – 40 mm |
| Longitud | 1000 – 6000 mm |
| Temple comunes | O, H111, H112, H116, H321, H32 |
| Elemento | Rango |
|---|---|
| Diámetro | 0,8 – 12 mm |
| Peso de la bobina | 10 – 500 kg |
| Tolerancia de tamaño | ± 0,05 mm |
| Temple comunes | O, H111, H112, H116, H321, H32 |
| Estándar | Denominación |
|---|---|
| AA (EE. UU.) | Aleación de aluminio 5086 |
| EN AW | AlMg4 |
| Serie | 5000 (Al-Mg, no tratable térmicamente) |
| Elemento | Peso % |
|---|---|
| Si | 0.40 máx. |
| Fe | 0,50 máx. |
| Cu | 0,10 máx. |
| Mn | 0.20 – 0.70 |
| Mg | 3.5 – 4.5 |
| Cr | 0.05 - 0.25 |
| Zn | 0,25 máx. |
| Ti | 0,15 máx. |
| Al | Saldo |
Los valores son rangos típicos de composición AA; confirmar contra la especificación solicitada y el MTC suministrado.
| Temple | Tracción (MPa) | Límite elástico (MPa) | Alargamiento (%) | Brinell |
|---|---|---|---|---|
| O | 275 | 115 | 15 | 65 |
| H111 | 305 | 180 | 14 | 75 |
| H112 | 280 | 130 | 14 | 70 |
| H116 / H321 | 325 | 230 | 12 | 80 |
| H32 | 325 | 230 | 12 | 80 |
Los valores mecánicos son típicos representativos a temperatura ambiente para placa, chapa o barra, y deben confirmarse contra el espesor solicitado y el MTC suministrado.
Elija el temple más blando que cumpla con el requisito de resistencia para mantener la conformabilidad y soldadura sencillas.
Good resistance to seawater and many industrial environments, suitable for hulls and offshore parts.
Welds readily with TIG/MIG and matching 5xxx filler; strength in the weld zone is close to the base metal.
Reaches useful strength through strain hardening, so no quenching or aging is needed.
5086 Aluminum Alloy is a non-heat-treatable 5xxx alloy, so strength comes from strain hardening (H-tempers), not heat treatment. It cuts, drills, and welds well with standard aluminum tooling.
Nota: el color anodizado de las aleaciones 5xxx puede diferir ligeramente del de las aleaciones 6xxx; confirme el acabado en una muestra si la coincidencia de color es importante.
Cada pedido de 5086 se envía con un Certificado de Ensayo de Fábrica (MTC) que informa el análisis químico real y los resultados mecánicos del material suministrado. Se pueden gestionar informes de ensayo de terceros SGS o equivalentes a solicitud para requisitos de proyectos o licitaciones.
Linsy Aluminum es un proveedor de aluminio con sede en Shenzhen con más de 20 años de experiencia sirviendo a clientes de los sectores marino, de transporte e ingeniería general. Suministramos material de las series 1000 a 8000 en formas de placa, barra, tubo, alambre, bobina, perfil y bloque.
Para obtener un presupuesto, comparta su aleación, temple, dimensiones, cantidad y cualquier requisito de certificación.
No. 5086 is a non-heat-treatable 5xxx alloy; its strength comes from magnesium content and strain hardening (H-tempers).
Matching 5xxx fillers such as 5356 or 5183 are commonly used, depending on the parent alloy and service conditions.
Both are marine-grade 5xxx alloys. 5083 (Mg ~4.0–4.9) is typically used for higher-strength plate; 5086 is chosen where its formability and corrosion profile fit the job. Confirm with your design specification.
Los tamaños personalizados suelen producirse en un plazo de 10 a 60 días, dependiendo de la aleación, el temple y la cantidad. Confirme el plazo al solicitar un presupuesto.
Sí. Se proporciona un MTC con cada pedido, y se pueden gestionar informes de ensayo de terceros bajo solicitud.
Acabado de laminación, anodizado, pulido, recubrimiento en polvo y film de PVC están disponibles según la forma del producto.
Apoyamos cantidades mínimas de pedido reducidas para solicitudes personalizadas. Comparta su tamaño y cantidad requeridos para obtener un presupuesto.
Ventajas de Linsy
Linsy Aluminum es un proveedor líder de productos de procesamiento de aluminio, que presta servicio a diversas industrias, como la aeroespacial, la ingeniería general, la automoción, la marina, la construcción naval y otras aplicaciones industriales especializadas.
Nos comprometemos a mantener los más altos estándares de calidad y responsabilidad medioambiental, como demuestran nuestras certificaciones: ISO 9001:2008， ISO 14001:2004 y SGS.