7175 is a high-strength 7xxx alloy designed for superior toughness — often favored over 7075 where fracture resistance matters more than peak strength. Linsy supplies 7175 plate, bar and tube in T74, T7452 and T7454 tempers with full MTC documentation for aerospace and high-stress applications.
Formularios disponibles: plate / sheet / bar / tube
Temperamentos habituales: T74 / T7452 / T7454
Asistencia técnica: CNC machining, forging support, anodizing
Documentos de calidad: Informe MTC con cada pedido
7175 is a high-strength 7xxx alloy designed for superior toughness — often favored over 7075 where fracture resistance matters more than peak strength. Linsy supplies 7175 plate, bar and tube in T74, T7452 and T7454 tempers with full MTC documentation for aerospace and high-stress applications. Its improved toughness helps it perform under stress and impact, making it a common choice for forged and machined aircraft parts.
| Espesor (mm) | Anchura (mm) | Longitud (mm) | Temple |
|---|---|---|---|
| 6 – 150 | 500 – 2500 | up to 12,000 | T74, T7452, T7454 |
| Custom sizes on request | — | — | — |
| Bar Dia. (mm) / Tube OD (mm) | Longitud (mm) | Temple | |
|---|---|---|---|
| 3 – 300 (bar) / 6 – 300 (tube) | up to 12,000 | T74, T7452, T7454 | |
| Custom sizes on request | — | — | — |
7175 is supplied to AMS and ASTM references where applicable (e.g., AMS 4341 for hand forgings). EN AW designation: EN AW-7175. Confirm exact spec with our team.
| Elemento | Contenido (%) |
|---|---|
| Si | 0,15 máx. |
| Fe | 0,20 como máximo |
| Cu | 1.2 - 2.0 |
| Mn | 0,10 máx. |
| Mg | 2.1 - 2.9 |
| Cr | 0.18 - 0.28 |
| Zn | 5.1 - 6.1 |
| Ti | 0,10 máx. |
| Otros (cada uno) | 0,05 máx. |
| Otros (total) | 0,15 máx. |
| Al | Saldo |
Typical T74/T745x values: tensile 520–590 MPa, yield 430–490 MPa, elongation 3.8–5.9%, shear 290–330 MPa. Confirm against the MTC for your form and thickness.
| Temple | Temple | Tracción (MPa) | Límite elástico (MPa) | Elong. (%) |
|---|---|---|---|---|
| T74 | 520 – 590 | 430 – 490 | 3.8 – 5.9 | |
| T7452 | 520 – 590 | 430 – 490 | 3.8 – 5.9 | |
| T7454 | 520 – 590 | 430 – 490 | 3.8 – 5.9 |
T74 / T7452 / T7454 — overaged tempers that maximize toughness and stress-corrosion resistance; T7452 is for die forgings, T7454 for hand forgings. Choose based on form and toughness needs.
Better fracture resistance than 7075 at slightly lower strength.
Machines well in overaged tempers.
Not recommended for fusion welding.
Aircraft structural forgings, gears and shafts, high-stress machine parts, automotive and aerospace components.
CNC machining supported; anodizing available. Overaged tempers machine more predictably than T6.
Every order ships with an MTC. SGS third-party test reports available on request. Linsy holds ISO 9001, ISO 14001 and ISO 45001.
Linsy Aluminum is a Shenzhen-based supplier with 20+ years of experience across the 1000–8000 series. We supply 7175 plate, bar and tube with MTC per order and support custom sizes. Typical custom lead time is 10–60 days.
Internal Linsy blog links for 7175 are being added as articles are published.
What tempers does 7175 come in?
T74, T7452 and T7454.
7175 vs 7075?
7175 trades some peak strength for higher toughness — better for impact/fatigue parts.
Lead time?
10–60 days for custom sizes.
MTC provided?
Yes, with every order.
Custom sizes?
Yes.
Standards?
AMS, ASTM, GB/T, EN on request.