6201 aluminum wire is a heat-treatable, electrical-grade alloy that balances high mechanical strength with good conductivity and corrosion resistance. Supplied mainly in the T81 temper, it is the standard choice for All Aluminum Alloy Conductors (AAAC) and overhead power lines. Linsy draws 6201 wire in a range of diameters and supports custom coil weights, tempers, and processing for utility and industrial projects.
Formularios disponibles: wire, sheet / coil / tube / bar / profile
Temperamentos habituales: T81, T6, T4, O
Asistencia técnica: Mecanizado CNC, corte por láser, soldadura TIG/MIG, anodizado, pulido, recubrimiento en polvo
Documentos de calidad: Informe MTC con cada pedido
6201 belongs to the 6000 series (Al-Mg-Si) and is optimized for electrical conductor use rather than general structural work. Compared with the classic 1350 EC grade, 6201 trades some conductivity for substantially higher strength, letting conductors carry heavier mechanical loads with smaller sags. The T81 temper (solution heat treated, cold worked, and artificially aged) delivers the best combination of strength and conductivity for overhead lines.
| Parámetro | Rango |
|---|---|
| Diámetro | 0.8 – 30 mm |
| Peso de la bobina | Minimum 50 kg, custom on request |
| Estados | O, T4, T6, T81 |
| Tolerancia de tamaño | ± 2% (typical) |
| Normas | ASTM B398/B398M, EN 573, GB/T 3190 |
6201 is also available as sheet, coil, tube, bar, and profile for non-conductor applications. Share your drawing or spec to receive a quote for these forms.
| Denominación | Referencia |
|---|---|
| AA / UNS | A96201 |
| EN AW | EN AW-6201 |
| Normas comunes | ASTM B398 (wire), ASTM B211, EN 755, GB/T 3191 |
| Product form focus | Drawn wire for AAAC conductors |
| Elemento | Contenido (wt%) |
|---|---|
| Silicio (Si) | 0,50 – 0,90 |
| Hierro (Fe) | 0,50 máx. |
| Cobre (Cu) | 0,10 máx. |
| Manganeso (Mn) | 0,03 máx. |
| Magnesio (Mg) | 0,60 – 0,90 |
| Cromo (Cr) | 0,10 máx. |
| Zinc (Zn) | 0,10 máx. |
| Titanio (Ti) | 0,03 máx. |
| Otros, cada uno | 0,05 máx. |
| Otros, total | 0,15 máx. |
| Aluminio (Al) | Saldo |
| Temple | Tracción (MPa) | Límite elástico (MPa) | Alargamiento (%) | Cortante (MPa) |
|---|---|---|---|---|
| T81 | 310 min | 275 min | 8 mín. | 193 |
| T6 | 300 – 330 | 260 – 290 | 8 – 12 | 185 – 195 |
| T4 | 200 – 240 | 110 – 140 | 12 – 16 | 150 – 165 |
| O | ≤ 150 | ≤ 90 | ≥ 18 | ≤ 95 |
Preferred conductor temper. Maximum strength with stable conductivity for overhead AAAC lines.
Good all-round strength for fittings and structural wire where full T81 cold work is not required.
Softer, more formable; used when bending or forming is needed before aging.
Annealed, lowest strength; seldom used for conductors but available for special forming.
Higher strength than 1350 EC wire while keeping useful conductivity for power transmission.
Good atmospheric and coastal corrosion resistance, suitable for exposed overhead lines.
Responds to solution heat treatment and aging for controlled temper properties.
Uniform drawn wire strands cleanly into compact AAAC conductors.
6201 wire is supplied drawn and aged; further cold working or re-aging is not normally required. It can be stranded, baked, and connectorized using standard utility practices. Anodizing is possible for identification but is uncommon on conductors. Welding of finished conductors is generally avoided; mechanical or compression joints are preferred.
Cada pedido se envía con un Certificado de Ensayo de Fábrica (MTC) que registra la composición y los resultados mecánicos. Nuestro sistema de calidad está certificado según ISO 9001, ISO 14001 e ISO 45001. Se pueden gestionar informes de ensayo SGS de terceros bajo solicitud. La inspección cubre dimensiones, condición superficial y verificación mecánica por temple.
Linsy Aluminum is a Shenzhen-based aluminum manufacturer with more than 20 years of experience supplying the 1000 to 8000 series in plate, bar, tube, wire, coil, profile, and block forms. For 6201 aluminum, we support both off-the-shelf ranges and made-to-order dimensions.
See the blog articles linked below for deeper background, and contact our team for a tailored quote on 6201 aluminum.
6201 typically provides about 52% IACS, lower than 1350 EC wire (about 61% IACS) but with significantly higher strength, which is the reason it is chosen for AAAC.
For conductors, T81 is preferred because the cold-work plus age step gives the highest strength at a stable conductivity. T6 is used where full cold work is not required.
Finished conductors are normally joined with compression or mechanical fittings rather than welding. Welding is not standard practice for strand-in-place lines.
Standard coils start at a 50 kg minimum with custom weights on request. Diameter range is 0.8 to 30 mm.
Los tamaños y temple personalizados suelen enviarse dentro de 10 a 60 días. Confirme el plazo exacto al solicitar una cotización, ya que depende de la aleación, el temple, las dimensiones y la cantidad del pedido.
La cantidad mínima de pedido (MOQ) es flexible y se evalúa caso por caso. Los lotes pequeños y prototipos a menudo pueden ser atendidos; las series más grandes o estándar resultan más económicas. Comparta sus dimensiones y cantidad requeridas para una cotización firme.
Cada pedido se envía con un Certificado de Prueba de Molino (MTC). Las certificaciones ISO 9001, ISO 14001 e ISO 45001 aplican a nuestro sistema de gestión. Se pueden gestionar informes de pruebas de terceros SGS bajo solicitud.
Sí. Ofrecemos mecanizado CNC, corte por láser, soldadura TIG/MIG y tratamientos superficiales que incluyen anodizado, pulido, recubrimiento en polvo y protección con película de PVC.
Envíe su aleación/temple, forma requerida, dimensiones, cantidad y cualquier requisito de procesamiento o certificación. Nuestro equipo devuelve una cotización con plazo de entrega y condiciones de envío.